Elemental partitioning effects due to crystal progress procedures in binary NiAl alloys are exposed. The directional solidification system is analysed concerning a solidification product of binary NiAl alloys getting regard to the composition dependent partition coefficient. The predictions are in comparison with electron probe microanalysis